牌號(hào)簡(jiǎn)介 About
OREVAC 18750是一種基于馬來酸酐改性聚丙烯樹脂的共擠出涂料膠粘劑。它以顆粒形式存在,可用于傳統(tǒng)的擠出和共擠設(shè)備,用于加工聚烯烴。應(yīng)用OREVAC 18750是一種用于擠出涂層和擠出層壓技術(shù)的粘結(jié)樹脂。它被設(shè)計(jì)成在這些工藝中與鋁箔、紙張或聚丙烯薄膜等基材形成粘合,并與聚丙烯和PA等樹脂共擠。Orevac 18750具有優(yōu)良的加工性能,特別是在拉伸性、縮頸性和熔融穩(wěn)定性方面。除了粘合性能外,OREVAC 18750的特殊配方還允許設(shè)計(jì)具有受控開啟力的聚丙烯或聚丙烯涂層杯和容器的鋁蓋。(*)對(duì)鋁箔的粘合性能很大程度上取決于層壓板的熱條件。冷鋁箔涂層的標(biāo)準(zhǔn)條件要求使用特殊的后熱處理,其中OREVAC層必須再次熔化。 OREVAC? 18750 is a coextrusion coating adhesive based on a maleic anhydride modified polypropylene resin. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyolefin. Applications OREVAC? 18750 is a tie resin to be used in extrusion coating and extrusion lamination technologies. It has been designed to develop adhesion in these processes onto substrates like aluminum foil (*), paper or PP films and in coextrusion with resins like PP and PA. OREVAC? 18750 exhibits excellent processing properties, particularly regarding drawability, neck-in and melt stability. In addition to adhesive properties, the special formulation of OREVAC? 18750 allows to design aluminum lids for PP or PP coated cups and containers with controlled opening forces. (*) Adhesion performance to aluminum foil is strongly dependant on thermal conditions in the laminator. Standard conditions of coating onto cold aluminum foil require using a specific post heating treatment in which the OREVAC layer must be molten again.

產(chǎn)品描述 Product Description
廠家:法國阿科瑪 Arkema 類別:PP均聚 PP homopolymerization 用途:鋁箔涂料;粘結(jié)樹脂;管線涂料;蓋子;層壓板;飲料蓋子;涂層應(yīng)用; 加工條件:共擠出成型 性能特點(diǎn): 無腐蝕性; 熱穩(wěn)定性好; 熔體穩(wěn)定性高; 粘結(jié)性好; 易剝離; 易加工; Excellent Processability,Good dissection,Non-corrosiveness,Good bond,Heat Stabilized,Higher melt stability
技術(shù)參數(shù) Technical Data
物理性能 額定值 Nominal Value 單位 Units 測(cè)試方法 Test Method
密度 Density g/cm3 ASTM D1505
密度 Density g/cm3 ISO 1183
熔體質(zhì)量流動(dòng)速率 熔體質(zhì)量流動(dòng)速率
230℃, 230℃/ kg 35 g/10min ISO 1133
230℃, 230℃/ kg 35 g/10min ASTM D1238
機(jī)械性能 額定值 Nominal Value 單位 Units 測(cè)試方法 Test Method
拉伸模量 拉伸模量
mm mm 500 MPa ISO 527-2
mm mm 500 MPa ASTM D638
拉伸強(qiáng)度 拉伸強(qiáng)度
屈服, mm 屈服, mm MPa ASTM D638
屈服, mm 屈服, mm MPa ISO 527-2
拉伸應(yīng)變 拉伸應(yīng)變
斷裂, mm 斷裂, mm > 700 % ASTM D638
斷裂, mm 斷裂, mm > 700 % ISO 527-2
熱性能 額定值 Nominal Value 單位 Units 測(cè)試方法 Test Method
維卡軟化溫度 Vicat Softening Temperature 121 ℃ ASTM D1525 2
維卡軟化溫度 Vicat Softening Temperature 121 ℃ ISO 306/A
熔融溫度 Melting Temperature 160 ℃ ISO 11357-3
備注
1 一般屬性:這些不能被視為規(guī)格。
2 壓 力1 (10N)