依凡坦33-25是由乙烯和醋酸乙烯經高壓自由基聚合而成的無規(guī)共聚物。乙烯基醋酸鹽含量高的Evatane 33-25具有柔軟性、柔韌性和極性。Evatane 33-25與大多數增粘樹脂和蠟兼容。它是一種高效易操作的熱熔膠配方產品。Evatane 33-25與大多數填料具有高粘合強度,可用于生產HFFR化合物。它也是一種理想的基礎聚合物,用于中壓電纜(外部可剝離層)的半導電化合物。 EVATANE? 33-25 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. The high Vinyl Acetate content of EVATANE? 33-25 brings softness, flexibility and polarity. EVATANE? 33-25 is compatible with most tackifying resins and waxes. It is an efficient and easy handling product for hot melt adhesives formulations. EVATANE? 33-25 delivers high cohesive strength with most fillers and can be used to produce HFFR compounds. It is also an ideal base polymer for semi-conductive compounds for medium voltage cables (external strippable layer).

產品描述 Product Description
廠家:法國阿科瑪 Arkema 類別:EVA EVA 用途:電線電纜應用;粘合劑; 性能特點: 柔軟性好; 無規(guī)共聚物; 韌性好; Good flexibility,Random copolymer,Soft
技術參數 Technical Data
物理性能 額定值 Nominal Value 單位 Units 測試方法 Test Method
密度 Density (73°F) g/cm3 ISO 1183
熔體質量流動速率 熔體質量流動速率
190℃, 190℃/ kg 22 to 29 g/10min ISO 1133
190℃, 190℃/ kg 22 to 29 g/10min ASTM D1238
醋酸乙烯含量 Vinyl Acetate Content to wt% Internal Method
機械性能 額定值 Nominal Value 單位 Units 測試方法 Test Method
邵氏硬度 邵氏硬度
邵氏 A 邵氏 A 67 ASTM D2240
邵氏 A 邵氏 A 67 ISO 868
拉伸強度 拉伸強度
斷裂 斷裂 MPa ISO 527-2
斷裂 斷裂 MPa ASTM D638
拉伸應變 拉伸應變
斷裂 斷裂 900 to 1100 % ISO 527-2
斷裂 斷裂 900 to 1100 % ASTM D638
熱性能 額定值 Nominal Value 單位 Units 測試方法 Test Method
維卡軟化溫度 Vicat Softening Temperature < ℃ ASTM D1525 2
維卡軟化溫度 Vicat Softening Temperature < ℃ ISO 306/A
熔融溫度 Melting Temperature ℃ ISO 11357-3
Ring and Ball Softening Point Ring and Ball Softening Point 3 3 119 ℃ ASTM E28
備注
1 一般屬性:這些不能被視為規(guī)格。
2 壓 力1 (10N)
3 NF EN 1238