OREVAC 18507是一種化學(xué)功能化高密度聚乙烯,具有高含量的順丁烯二酸酐。接枝馬來酸酐具有極性,對天然纖維和礦物填料具有優(yōu)異的粘附性能。應(yīng)用OREVAC 18507被設(shè)計成用作無鹵阻燃電纜化合物中的偶聯(lián)劑。它具有優(yōu)異的機(jī)械性能、高的斷裂拉伸強(qiáng)度和良好的延伸率、良好的耐磨性和良好的耐化學(xué)性。OREVAC 18507也適用于在高密度聚乙烯樹脂和礦物填料或天然纖維之間形成可靠的粘合強(qiáng)度。 OREVAC? 18507 is a chemically functionalized high-density polyethylene with a high content of maleic anhydride. Grafted maleic anhydride induces polarity and leads to outstanding adhesion properties on natural fibers and mineral fillers. Applications OREVAC? 18507 has been designed to be used as coupling agent in halogen free flame retardant cable compounds. It provides outstanding mechanical properties, high tensile strength at break and good elongation, good abrasion and good chemical resistance. OREVAC? 18507 is suitable also to develop a reliable bonding strength between HDPE resins and mineral filler or natural fibers.

產(chǎn)品描述 Product Description
廠家:法國阿科瑪 Arkema 類別:HDPE HDPE 用途:塑料改性; 加工條件:擠出 Extrusion 性能特點: 拉伸性能好; 耐磨; 耐化學(xué)性; 粘結(jié)性好; Good bond,Good Tensile Strength,Good wear resistance,Solvent resistance
技術(shù)參數(shù) Technical Data
物理性能 額定值 Nominal Value 單位 Units 測試方法 Test Method
密度 Density g/cm3 ASTM D1505
密度 Density g/cm3 ISO 1183
熔體質(zhì)量流動速率 熔體質(zhì)量流動速率
190℃, 190℃/ kg g/10min ISO 1133
190℃, 190℃/ kg g/10min ASTM D1238
機(jī)械性能 額定值 Nominal Value 單位 Units 測試方法 Test Method
邵氏硬度 邵氏硬度
邵氏 D,模壓成型 邵氏 D,模壓成型 66 ISO 868
邵氏 D,模壓成型 邵氏 D,模壓成型 66 ASTM D2240
拉伸強(qiáng)度 拉伸強(qiáng)度
斷裂,模壓成型 斷裂,模壓成型 MPa ASTM D638
斷裂,模壓成型 斷裂,模壓成型 MPa ISO 527-2
拉伸應(yīng)變 拉伸應(yīng)變
斷裂,模壓成型 斷裂,模壓成型 800 % ISO 527-2
斷裂,模壓成型 斷裂,模壓成型 800 % ASTM D638
熱性能 額定值 Nominal Value 單位 Units 測試方法 Test Method
熔融溫度 Melting Temperature 128 ℃ ISO 11357-3
備注
1 一般屬性:這些不能被視為規(guī)格